Fabrication of CNTs/AlSi7Mg Composites and its Mechanical Properties

Zeng Gang; Zeng Xiaoshu; Wu Shengwei; Wei Jiaqi

doi:10.15980/j.tzzz.2013.02.004

Views : 0 下载量: 212 CSCD: 3

Export
Share
Collection
Album

Fabrication of CNTs/AlSi7Mg Composites and its Mechanical Properties
Vol. 33, Issue 2, Pages: 170-173(2013)
Published： 2013 ，
DOI： 10.15980/j.tzzz.2013.02.004

扫描看全文

[1]曾刚,曾效舒,邬胜伟,魏嘉麒.碳纳米管增强AlSi7Mg合金的制备及力学性能[J].特种铸造及有色合金,2013,33(02):170-173.

Zeng Gang, Zeng Xiaoshu, Wu Shengwei, et al. Fabrication of CNTs/AlSi7Mg Composites and its Mechanical Properties. [J]. Special Casting & Nonferrous Alloys 33(2):170-173(2013)
[1]曾刚,曾效舒,邬胜伟,魏嘉麒.碳纳米管增强AlSi7Mg合金的制备及力学性能[J].特种铸造及有色合金,2013,33(02):170-173. DOI： 10.15980/j.tzzz.2013.02.004.

Zeng Gang, Zeng Xiaoshu, Wu Shengwei, et al. Fabrication of CNTs/AlSi7Mg Composites and its Mechanical Properties. [J]. Special Casting & Nonferrous Alloys 33(2):170-173(2013) DOI： 10.15980/j.tzzz.2013.02.004.

摘要

将普通碳纳米管、化学包覆镍碳纳米管分别与铝粉按质量比1:5混合球磨后压制成块

采用钟罩将碳纳米管预制块压入铝合金熔体制备CNTs/AlSi7Mg复合材料。测试了复合材料的室温力学性能

通过X射线衍射仪（XRD）、扫描电镜（SEM）和能谱分析仪（EDS）对复合材料及其断口进行观察与分析。结果表明

碳纳米管的加入能细化复合材料的组织

使复合材料的二次枝晶臂间距减小

明显提高复合材料的抗拉强度、硬度和弹性模量。化学包覆镍碳纳米管加入量为1.0%时

T6态复合材料的抗拉强度、硬度（HV）和弹性模量分别达到了306MPa、118和132GPa

比基体提高了33.4%、25.5%和53.9%。复合材料的断口呈准解理型脆性断裂的特征。

Abstract

Preforms were prepared with commercial carbon nanotubes、Ni-CNTs and Al with the mass ratio of 1:5.Then the CNTs/AlSi7Mg composites were produced by immersing the preforms into the aluminum alloy melt with bell jar.The ambient mechanical properties of the composites were tested

and the structure and tensile fracture morphology of the composites were observed and analyzed by X-ray diffractometry（XRD）、scanning electron microscopy（SEM）and energy dispersive spectrum analysis（EDS）.The results show that with CNTs addition

the grains of the composite can be refined

and the secondary dendrite arm space of the composites is reduced.Meanwhile

the tensile strength

the microhardness and the elastic modulus of the composites are improved significantly.The tensile strength

the micro-hardness HV and the elastic modulus of the composites with 1.0%CNTs reach 306MPa、118.0 and 132GPa

respectively

increased by 33.4% 、25.5%and 53.9%

respectively

compared with those of the matrix alloy.The fracture of the composites is characterized by quasi-cleavage type brittle fracture.