5B01 alloy sheet was prepared by semi-continuous casting-rolling technology.Influences of stabilizing annealing on the mechanical properties

exfoliation corrosion resistance and texture of the cold rolling sheet were investigated.The results show that

with increasing in stabilizing annealing temperature

strength of the alloy is decreased and elongation is increased

however

exfoliation corrosion resistance of the alloy is increased firstly and then decreased.There are mainly Brass{011}(211)

Copper{112}(111) and S{123}<634> texture in cold-rolled Al-Mg alloy sheets.With the annealing temperature increasing to 300 ℃

the deformed textures disappear gradually

and the brass and copper textures are evolved into cube{001}(100) and cube-rotation{001}(110) textures.