Constitutive Equation of High Temperature Deformed Hot Working Mg-Zn-Y-Zr Magnesium Alloy

Hu Chuankai1; Chen Qiang1; Shu Dayu1; Zhao Zude1; Lin Jun1; Wang Yanbin1

doi:10.15980/j.tzzz.2012.03.021

Views : 0 下载量: 263 CSCD: 2

Export
Share
Collection
Album

Constitutive Equation of High Temperature Deformed Hot Working Mg-Zn-Y-Zr Magnesium Alloy
Vol. 32, Issue 3, Pages: 220-223(2012)
Published： 2012 ，
DOI： 10.15980/j.tzzz.2012.03.021

扫描看全文

[1]胡传凯,陈强,舒大禹,赵祖德,林军,王艳彬.镁合金Mg-Zn-Y-Zr的高温变形及本构方程[J].特种铸造及有色合金,2012,32(03):220-223.

Hu Chuankai1, Chen Qiang1, Shu Dayu1, et al. Constitutive Equation of High Temperature Deformed Hot Working Mg-Zn-Y-Zr Magnesium Alloy. [J]. Special Casting & Nonferrous Alloys 32(3):220-223(2012)
[1]胡传凯,陈强,舒大禹,赵祖德,林军,王艳彬.镁合金Mg-Zn-Y-Zr的高温变形及本构方程[J].特种铸造及有色合金,2012,32(03):220-223. DOI： 10.15980/j.tzzz.2012.03.021.

Hu Chuankai1, Chen Qiang1, Shu Dayu1, et al. Constitutive Equation of High Temperature Deformed Hot Working Mg-Zn-Y-Zr Magnesium Alloy. [J]. Special Casting & Nonferrous Alloys 32(3):220-223(2012) DOI： 10.15980/j.tzzz.2012.03.021.

摘要

采用Gleeble-1500热模拟试验机对铸态镁合金Mg-Zn-Y-Zr在变形温度为250～450℃

应变速率为0.001～1s-1条件下的高温压缩变形行为进行研究

利用双曲正弦关系描述了该合金的本构方程。结果表明

Mg-Zn-Y-Zr合金的高温流动应力-应变曲线主要以动态回复和动态再结晶软化机制为特征

峰值应力随变形温度的降低或应变速率的升高而增加;在真实应力-应变曲线基础上

建立的Mg-Zn-Y-Zr合金高温变形的本构模型较好地表征了其高温流变特性。

Abstract

High temperature compressive behavior of as-cast Mg-Zn-Y-Zr magnesium alloy was investigated on Gleeble-1 500 at 250-450 ℃ and strain rate from 0.001 to 1 s-1.Constitutive equation of the alloy was described by hyperbolic sine function.The results show that the stress-strain curves are characterized by softening mechanism of dynamic recovery and dynamic recrystallization

and the peak stress is increased with the decrease of deforming temperature

or the increase of strain rate.Constitutive equation of high temperature deformed Mg-Zn-Y-Zr magnesium alloy is well accordant with the high temperature deformation characteristics based on true stress-true strain curves.