Simulation of Fine Grain Casting Process of Superalloy K4202 by Thermal Control Method
Vol. 32, Issue 3, Pages: 223-226(2012)
Published： 2012 ，
DOI： 10.15980/j.tzzz.2012.03.001

扫描看全文

[1]王鹏飞,胡锐,钟宏,李金山,赵京晨.高温合金K4202热控法细晶铸造过程模拟[J].特种铸造及有色合金,2012,32(03):223-226.

Wang Pengfei1, Hu Rui1, Zhong Hong1, et al. Simulation of Fine Grain Casting Process of Superalloy K4202 by Thermal Control Method. [J]. Special Casting & Nonferrous Alloys 32(3):223-226(2012)
[1]王鹏飞,胡锐,钟宏,李金山,赵京晨.高温合金K4202热控法细晶铸造过程模拟[J].特种铸造及有色合金,2012,32(03):223-226. DOI： 10.15980/j.tzzz.2012.03.001.

Wang Pengfei1, Hu Rui1, Zhong Hong1, et al. Simulation of Fine Grain Casting Process of Superalloy K4202 by Thermal Control Method. [J]. Special Casting & Nonferrous Alloys 32(3):223-226(2012) DOI： 10.15980/j.tzzz.2012.03.001.

摘要

采用有限元软件模拟了高温合金K4202复杂薄壁件在低过热度浇注条件下的流场、温度场和凝固组织。结果表明

K4202高温合金复杂薄壁件在低过热度浇注时可以获得充型完整的铸件;高温合金K4202复杂薄壁铸件的厚大部位和变截面部分易出现缩松缺陷;当高温合金在低过热度浇注时

铸件整体获得了等轴晶均匀分布的细晶组织

晶粒度达ASTM2-3。

Abstract

The flow field

temperature field and microstructure of complex thin-walled superalloy K4202 castings were simulated with the help of the finite element software.The results show that

with a well established filling system

the thin-walled castings can be well filled in the condition of low super-heating.According to the temperature field

the shrinkage porosity easily occurs in the thick wall location or the location with variable cross-sections.With the low super-heating pouring

the uniform structure with the grain size ASTM2-3 can be observed in the whole castings.

关键词

K4202合金低过热度熔模铸造充型性凝固

Keywords

Superalloy K4202Low Super-HeatingInvestment CastingFillingSolidification

references

Alert me when the article has been cited

提交

Numerical Simulation of Sintering Temperature Field in Titanium Alloy Investment Casting Shell

Effects of Upward Continuous Casting Parameters on Solidification Behavior of Oxygen-free Copper Billets

Data Acquisition and Production Intelligent Prediction in Casting Workshop

Discussion on Investment Casting Process of Valve Body With Concentrated Hot Spot