      • Pan Ye Sun Guoxing
        Issue 5, Pages: 1-3(1993)
        摘要：Iron phase morphology and properties of Al-Si alloys containing night Fe Content at different conditions were investigated. It was shown that the appearance of primary iron phase was changed from coarse needle-plate form to fine short plate, polyhedron, Chinese script and granular form after Mn addition or high temperature superheat treatment. The mechanical property and castability of the alloys were obviously increased and improved respectively. The fracture model of the alloys with modified and unmodified iron phase was also analyzed  
        关键词：铁相形态;铝合金;性能   
        2
        |
        480
        |
        80
        <HTML>
        <Meta-XML>
        <引用本文> <批量引用> 46193567 false
        发布时间：2023-12-18
      • Bao Yankun Yu Liancong Kuang Agen Xu Liwen
        Issue 5, Pages: 4-8(1993)
        摘要：The Rheological and technological properties of colloidal silica sol sllurry and the influencing factors were studied. It was shown that the yield value of colloidal silica sol slurry was increased and its suspensibility was improved by adding some additives. The mechanism for these improvements was discussed.  
        关键词：硅溶胶涂料;流变性;工艺性   
        2
        |
        262
        |
        13
        <HTML>
        <Meta-XML>
        <引用本文> <批量引用> 46192085 false
        发布时间：2023-12-18
      • Zhang Shoukui
        Issue 5, Pages: 9-11(1993)
        摘要：The microstructures of hypereutectic Al-Si alloys under rotary magnetic field have been studied. Experimental results show the primary Si grain can be refined , and the specimen surface a rich primary Si area can be obtained. So wear property of the alloys is improved. The better effect may be obtained when rotary inagnetic field condition unite with modification with phosphorus.  
        关键词：旋转磁场;初生硅富集;过共晶铝硅合金   
        2
        |
        88
        |
        12
        <HTML>
        <Meta-XML>
        <引用本文> <批量引用> 46193072 false
        发布时间：2023-12-18
      • Lin Youdong Yuan Zhongyue Zhang Zhongming Liu Baodi
        Issue 5, Pages: 12-14(1993)
        摘要：The carbon pick-up of cast steel ZG25 was studied by changing the technology factors such as coating permeability, coating thinkness vaccum degree,etc. The opinion that the carbon pick-up would be mainly occured between the interface of metal and mold was put forward, and which would be easily restrained by reducing the deposit concentration of EPS degradation products at the surface of the mold.  
        关键词：消失模;铸钢件增碳   
        2
        |
        78
        |
        15
        <HTML>
        <Meta-XML>
        <引用本文> <批量引用> 46193134 false
        发布时间：2023-12-18
      • Yu Libo Xin Mingde
        Issue 5, Pages: 15-17(1993)
        摘要：In this paper the structure and hardness performances of Cu-Cr-Zr-Mg alloy under casting state, solid solution quenching, cold deformation and ageing treatment were investigated. The changes of the structure and hardness at diffenrent time and ageing temperature,after the alloy had taken place more 40% cold deformation, were analysed. The optimum ageing process was determined. The thermology performance and mechanical nature of the alloy were also measued. All results showed that this kind of copper alloy belongs to the middle strength and high conductive alloy.  
        关键词：Cu-Cr-Zr-Mg合金;热学与力学性能   
        2
        |
        38
        |
        0
        <HTML>
        <Meta-XML>
        <引用本文> <批量引用> 46192749 false
        发布时间：2023-12-18
      • Xu Jiping Mao Yiyuan Xu Zhichang Ji Weizhi
        Issue 5, Pages: 18-21(1993)
        摘要：The equipment , mould structure and processing of manufacturing aluminum alloy handle stems of bicycle using extrusion casting method are presented. By testing, it is determined that this is an effective method of manufacturing high quality aluminum alloy handle stems with high comprehensive mechanical properties.  
        关键词：铝合金;把主管   
        2
        |
        31
        |
        1
        <HTML>
        <Meta-XML>
        <引用本文> <批量引用> 46192137 false
        发布时间：2023-12-18
      • Issue 5, Pages: 22-25(1993)
        摘要：阐述了铸造蒙乃尔合金的化学成分、金相组织、机械性能和耐蚀性能。着重分析了蒙乃尔合金的吸气、氧化、收缩等熔铸冶金特性。作者指出;只要采取正确的熔炼工艺并对合金熔体进行适当的处理,在非真空条件下完全可以生产出优质的蒙乃尔合金铸件。  
        关键词：蒙乃尔;镍铜合金;冶金特性   
        2
        |
        225
        |
        9
        <HTML>
        <Meta-XML>
        <引用本文> <批量引用> 46193720 false
        发布时间：2023-12-18
      • Issue 5, Pages: 26-28(1993)
        摘要：卧式压铸机采用中心浇口时,存在着浇口余料的切断问题。本文详细地介绍了开模时利用斜导住驱动的滑块切断机构的结构及工艺参数的设计。  
        关键词：浇口余料;斜导柱;滑块   
        2
        |
        28
        |
        0
        <HTML>
        <Meta-XML>
        <引用本文> <批量引用> 46193049 false
        发布时间：2023-12-18
      • Issue 5, Pages: 29-30(1993)
        摘要：介绍了Al-Li合金用保护气氛的熔铸设备,它具有独特的半封闭式结构,能有机地将Al-Li合金熔炼与半连续铸造结合为一体,设备结构简单,操作方便,造价低廉,创造性地解决了防止锂的氧化,锂的烧损率在3％以下,该设备适用于Al-Li合金的熔铸。  
          
        2
        |
        66
        |
        0
        <HTML>
        <Meta-XML>
        <引用本文> <批量引用> 46192706 false
        发布时间：2023-12-18
      • Issue 5, Pages: 31-32(1993)
        摘要：<正> 1 前言 水玻璃目前仍然是国内熔模铸造中使用最多的制壳粘结剂,国内对水玻璃型壳已进行了大量研究,对于各种不同工艺因素对水玻璃型壳性能的影响已经有了比较充分的认识。但是熔模铸造工作者更希望能直接量化型壳的性能,以便通过性能预测控制制壳过程,帮助分析废品产生原因,提高铸件质量。为此,本文在水玻璃型壳强度研究的基础上,进一步开发了熔模铸造水玻璃型壳性能的预测系统。  
          
        4
        |
        51
        |
        1
        <HTML>
        <Meta-XML>
        <引用本文> <批量引用> 46193240 false
        发布时间：2023-12-18
      • Issue 5, Pages: 33-34(1993)
        摘要：<正> 1 前言 用陶瓷型浇铸模具的工艺在世界各国受到日益广泛的应用,特别是那些机加工难于成形的模具,该法更具得天独厚的优势,其优点是用这种工艺所生产的铸件,尺寸精度高、表面光洁,可以部分或全部免去机加工,从而降低模具的生产成本。  
          
        2
        |
        32
        |
        18
        <HTML>
        <Meta-XML>
        <引用本文> <批量引用> 46193281 false
        发布时间：2023-12-18
      • Issue 5, Pages: 35-36(1993)
        摘要：<正> 广州标制汽车公司为实现标致504汽车国产化,决定试制三件橡胶地毯,其中前通道地毯为装配在发动机和变速箱上由多种圆弧面构成的曲面地毯,地毯形状复杂,模具制作困难。为了减轻橡胶生产工人的劳动强度,缩短开模周期,我们决定采用铸铝为地毯橡胶模具的成型上下模材料。橡胶模具如图1所示。  
          
        2
        |
        31
        |
        0
        <HTML>
        <Meta-XML>
        <引用本文> <批量引用> 46192896 false
        发布时间：2023-12-18
      • Issue 5, Pages: 36(1993)
        摘要：<正> 在辽宁南票矿务局精铸造型材料厂的支持下,中国铸协精铸专业委员会第三届年会于1993年8月5日至8日在兴城市召开。到会代表240余人,他们来自全国的100余家企业和大学、研究所。应大会邀请,美国及台湾地区的5家公司和大陆的20家精铸设备及原辅材料企业的代表也参加了大会。  
          
        2
        |
        3
        |
        0
        <HTML>
        <Meta-XML>
        <引用本文> <批量引用> 46193104 false
        发布时间：2023-12-18
      • Issue 5, Pages: 37-21(1993)
        摘要：<正> 我厂生产的大型铝铸件上箱体、下箱体、传动箱体采用湿砂型低压铸造生产工艺。1 概况1.1 铸件形状尺寸 上、下箱体、传动箱体最大壁厚为50mm,最小壁厚为14mm,几何形状复杂,壁厚不均,热节较多。  
          
        3
        |
        50
        |
        0
        <HTML>
        <Meta-XML>
        <引用本文> <批量引用> 46193026 false
        发布时间：2023-12-18
      • Issue 5, Pages: 38(1993)
        摘要：<正> 1 构造及原理 该设计采用油或煤气为燃料,以辐射的形式加热,见图1。为利用余热,在炉的底层设有排烟通道。这样,废气经后墙进入底层,重新给炉体补给热量,起加热保温作用。  
          
        2
        |
        13
        |
        0
        <HTML>
        <Meta-XML>
        <引用本文> <批量引用> 46193010 false
        发布时间：2023-12-18
      • Issue 5, Pages: 39(1993)
        摘要：<正> 还原罐是皮江法炼镁生产工艺的主要设备之一。要求还原罐能在1200℃高温和罐内壁3～10Pa真空条件下长期工作。因此罐材需具有良好的高温强度、高温抗氧化性和高温腐蚀性能,还要求罐材有高温组织稳定性和良好的焊接等加工性能。还原罐材质选用最近研制的MF-01高铬低镍稀土耐热合金。还原罐由前部水冷却套、中部耐热合金罐体和后部耐热合金封头三部份拼装焊接组成。罐体的尺寸为φ325mm×32mm×2700mm,重500kg左右。罐粗大,罐体质量要求很高,制作耐热合金罐体的技术难度较难。89年试制以来,已生产了300余个还原罐,平均使用寿命达到8个月。  
          
        2
        |
        71
        |
        5
        <HTML>
        <Meta-XML>
        <引用本文> <批量引用> 46194295 false
        发布时间：2023-12-18
      • Issue 5, Pages: 40-41(1993)
        摘要：<正> 1 问题的提出 我厂生产的疏水阀体系列产品内腔结构复杂,特别是在内腔中有一360℃环形槽,见图1。在生产中采用砂芯来满足工艺要求,但漂芯缺陷时有发生,特别是40、50疏水阀体漂芯废品率高达60％以上,严重地影响了产品质量和经济效益。  
          
        2
        |
        32
        |
        0
        <HTML>
        <Meta-XML>
        <引用本文> <批量引用> 46193624 false
        发布时间：2023-12-18
      • Issue 5, Pages: 42-43(1993)
        摘要：<正> 在熔模精密铸造中,如果铸件较小时,铸件都是通过内浇口与浇口棒直接相连的。在这一种浇注系统中,内浇口的形状、尺寸、位置等都与铸件质量有密切关系。本文主要探索内浇口面积不变时截面形状和内浇口位置对铸件质量的影响。1 内浇口截面形状对铸件质量的影响 图1所示铸件,材质为ZG60,重量为297g,内  
          
        2
        |
        63
        |
        0
        <HTML>
        <Meta-XML>
        <引用本文> <批量引用> 46194337 false
        发布时间：2023-12-18
      • Issue 5, Pages: 44(1993)
        摘要：<正> 柴油泵壳体CRF1-110-01系公司新开发民品柴油泵（大马力）主体零件,铸件质量关系着油泵性能和开发前景,原采用单边缝隙浇注成品率低,报废率高达85％,对铸件浇注系统工艺改进后合格率高达97％。1 铸件工艺性分析及技术要求 柴油泵壳体。铸件材料ZL-101,铸件重量12.7kg,用0.3MPa空气压力在煤油中检查内腔和孔的密封性,时间保持3min。根据铸件结构特点及技术要求,为保证铸件气密性要求,采用金属型铸造。  
          
        3
        |
        41
        |
        0
        <HTML>
        <Meta-XML>
        <引用本文> <批量引用> 46192994 false
        发布时间：2023-12-18
      • Issue 5, Pages: 44(1993)
        摘要：<正> 由械机工业部济南铸锻研究所设计、荆门铸造机械厂生产制造的S523型树脂砂旧砂再生成套设备于6月24日在湖北省老河口市组合机床厂通过了省级鉴定。 来自北京、天津、四川、广西、湖北等39个单位共62位用户、专家、学者、代表出席了会议并现场参观了S523型树脂砂再生成套设备的全部运行过程。由用户详细介绍了设备的使用情况,大家对国家铸锻机械质量监督检验中心所作的检测试验报告进行了认真的审查和讨论。  
          
        2
        |
        4
        |
        0
        <HTML>
        <Meta-XML>
        <引用本文> <批量引用> 46193185 false
        发布时间：2023-12-18
      • Issue 5, Pages: 45(1993)
        摘要：<正> 在过去的十五年中,美国的压铸工业悄然出现了一个新的现象:旧的压铸机越来越多地被重建或翻新,重新投入生产运转,有人称之为压铸机的“回收再用”。 重建,是将用过的压铸机彻底整修,恢复到原来压铸机生产厂家给定的性能指标;翻新,则是在重建的基础上增添或加强了某些功能,使翻新后的机器在技术先进性和性能参数方面均能与当今最先进的新压铸机相比。  
          
        2
        |
        11
        |
        0
        <HTML>
        <Meta-XML>
        <引用本文> <批量引用> 46193609 false
        发布时间：2023-12-18