The Study of Inner-Channel Defects Forming Mechanism in the Continuous Casting Grey Iron Pipe

Views : 0 下载量: 6 CSCD: 0

The Study of Inner-Channel Defects Forming Mechanism in the Continuous Casting Grey Iron Pipe
Issue 6, Pages: 12-15(1988)
Published： 1988 ，
DOI：

扫描看全文

[1]曹浩林,王箕.连续铸造灰铁管内沟缺陷形成机理的探讨[J].特种铸造及有色合金,1988(06):12-15.

The Neimenggu Polytechnic Institute Cao Hao Lin Wang Ji. The Study of Inner-Channel Defects Forming Mechanism in the Continuous Casting Grey Iron Pipe. [J]. Special Casting & Nonferrous Alloys (6):12-15(1988)
[1]曹浩林,王箕.连续铸造灰铁管内沟缺陷形成机理的探讨[J].特种铸造及有色合金,1988(06):12-15. DOI：

The Neimenggu Polytechnic Institute Cao Hao Lin Wang Ji. The Study of Inner-Channel Defects Forming Mechanism in the Continuous Casting Grey Iron Pipe. [J]. Special Casting & Nonferrous Alloys (6):12-15(1988) DOI：

本文通过测量内结晶器的变形

研究了内沟与石墨化膨胀及内结晶器变形的关系

指出了产生内沟的原因及其位置。为减少内沟采取措施提供了一定的依据。

The relationship among inner channel defect grapbitizing expesion

and inner crystallizer deformataon was investigatad by measuring inner crystallizer deformation

and it is pointed out why the inner channel is presented

and where it is located

therefore

the reason for measurem-ents of reducing the inner channel is represented.