Restraining the Carbon Pick-up in Steel Castings by Evaporative Pattern Process

Views : 0 下载量: 78 CSCD: 15

扫描看全文

[1]林尤栋,袁中岳,张忠明,刘宝弟.消失模铸钢件抑制增碳的研究[J].特种铸造及有色合金,1993(05):12-14+11.

Lin Youdong Yuan Zhongyue Zhang Zhongming Liu Baodi. Restraining the Carbon Pick-up in Steel Castings by Evaporative Pattern Process. [J]. Special Casting & Nonferrous Alloys (5):12-14(1993)
[1]林尤栋,袁中岳,张忠明,刘宝弟.消失模铸钢件抑制增碳的研究[J].特种铸造及有色合金,1993(05):12-14+11. DOI：

Lin Youdong Yuan Zhongyue Zhang Zhongming Liu Baodi. Restraining the Carbon Pick-up in Steel Castings by Evaporative Pattern Process. [J]. Special Casting & Nonferrous Alloys (5):12-14(1993) DOI：

通过改变涂料透气性、涂层厚度和真空度等工艺因素对ZG25增碳影响的试验研究

提出了增碳过程主要发生在金属和铸型的界面的见解。认为降低EPS分解产物在铸型表面的沉积浓度有利于抑制铸钢件的增碳。

The carbon pick-up of cast steel ZG25 was studied by changing the technology factors such as coating permeability

coating thinkness vaccum degree

etc. The opinion that the carbon pick-up would be mainly occured between the interface of metal and mold was put forward

and which would be easily restrained by reducing the deposit concentration of EPS degradation products at the surface of the mold.

消失模铸钢件增碳

消失模铸钢件增碳