Study on the Permology Performance and Mechanical Nature of Cu-Cr-Zr-Mg alloy
Issue 5, Pages: 15-17(1993)
Published： 1993 ，
DOI：

扫描看全文

[1]于立波,辛明德,牛世凤.Cu-Cr-Zr-Mg合金热学与力学性能的研究[J].特种铸造及有色合金,1993(05):15-17+25.

Yu Libo Xin Mingde. Study on the Permology Performance and Mechanical Nature of Cu-Cr-Zr-Mg alloy. [J]. Special Casting & Nonferrous Alloys (5):15-17(1993)
[1]于立波,辛明德,牛世凤.Cu-Cr-Zr-Mg合金热学与力学性能的研究[J].特种铸造及有色合金,1993(05):15-17+25. DOI：

Yu Libo Xin Mingde. Study on the Permology Performance and Mechanical Nature of Cu-Cr-Zr-Mg alloy. [J]. Special Casting & Nonferrous Alloys (5):15-17(1993) DOI：

摘要

研究了Cu-Cr-Zr-Mg合金的热学和力学性能。结果表明

该合金经40％以上的冷变形

再时效处理

硬度可达HB]65以上

抗拉强度可超过545MPa

延伸率不低于10％

导电率％IACS达70以上。

Abstract

In this paper the structure and hardness performances of Cu-Cr-Zr-Mg alloy under casting state

solid solution quenching

cold deformation and ageing treatment were investigated. The changes of the structure and hardness at diffenrent time and ageing temperature

after the alloy had taken place more 40% cold deformation

were analysed. The optimum ageing process was determined. The thermology performance and mechanical nature of the alloy were also measued. All results showed that this kind of copper alloy belongs to the middle strength and high conductive alloy.

关键词

Cu-Cr-Zr-Mg合金热学与力学性能

Keywords

Cu-Cr-Zr-Mg合金热学与力学性能