The Technology of Continuous Up\|Casting of Aluminium\|Pole
Issue S1, (1999)
Published： 1999 ，
DOI：

扫描看全文

[1]邹启明,彭立明,温宏权,毛协民,王海江.铝杆上引连铸技术探讨[J].特种铸造及有色合金,1999(S1):95-96.

Zou QimingPeng Liming\ Wen Hongquan\ Mao Xiemin\ Wang Haijiang. The Technology of Continuous Up\|Casting of Aluminium\|Pole. [J]. Special Casting & Nonferrous Alloys (S1).(1999)
[1]邹启明,彭立明,温宏权,毛协民,王海江.铝杆上引连铸技术探讨[J].特种铸造及有色合金,1999(S1):95-96. DOI：

Zou QimingPeng Liming\ Wen Hongquan\ Mao Xiemin\ Wang Haijiang. The Technology of Continuous Up\|Casting of Aluminium\|Pole. [J]. Special Casting & Nonferrous Alloys (S1).(1999) DOI：

摘要

简述了近年来对铝杆上引连铸技术的研究工作及取得的成果，浅析了影响铝杆上引连铸技术的关键问题，并对上引铝杆断杆机制作了探讨。研究表明，石墨与铝的反应扩散是导致拉断的内在原因，消除残留在结晶器上的铝环是解决拉断的途径

Abstract

The study of technology and achievements of continuous up\|casting of aluminium\|pole in recent years was described. Several key factors that affect aluminium\|pole up\|continuous casting were analyzed

and the mechanism of aluminium\|pole breaking was discussed. The results showed that the diffuse reaction between aluminium and graphite was the internal cause leading to break\|off

eliminate rdsidual aluminium\|ring on the crystallizer was the approach of sovling the problem.\=