Deformed Microstructure and the Eutectic Melting Activity Energy of AZ91D Magnesium Alloy by SIMA Method

Wang   Wuxiao  1; 2  Chen Jianjie2  Jiang Bailing2  Yuan Sen2  Jie Wanqi1

Views : 0 下载量: 202 CSCD: 3

Export
Share
Collection
Album

Deformed Microstructure and the Eutectic Melting Activity Energy of AZ91D Magnesium Alloy by SIMA Method
Issue 4, Pages: 205-207(2005)
Published： 2005 ，
DOI：

扫描看全文

[1]王武孝,程健杰,蒋百灵,袁森,介万奇.AZ91D合金SIMA形变组织与共晶熔化激活能的研究[J].特种铸造及有色合金,2005(04):205-207+189-190.

Wang Wuxiao 1, 2 Chen Jianjie2 Jiang Bailing2 Yuan Sen2 Jie Wanqi1. Deformed Microstructure and the Eutectic Melting Activity Energy of AZ91D Magnesium Alloy by SIMA Method. [J]. Special Casting & Nonferrous Alloys (4):205-207(2005)
[1]王武孝,程健杰,蒋百灵,袁森,介万奇.AZ91D合金SIMA形变组织与共晶熔化激活能的研究[J].特种铸造及有色合金,2005(04):205-207+189-190. DOI：

Wang Wuxiao 1, 2 Chen Jianjie2 Jiang Bailing2 Yuan Sen2 Jie Wanqi1. Deformed Microstructure and the Eutectic Melting Activity Energy of AZ91D Magnesium Alloy by SIMA Method. [J]. Special Casting & Nonferrous Alloys (4):205-207(2005) DOI：

摘要

研究了SIMA法制备半固态AZ91D镁合金坯料过程中形变率对形变组织的影响

并采用DSC技术研究了形变率与共晶熔化激活能的关系。结果表明:随着形变率的增大

合金的原始组织由树枝晶演变为碎块晶

晶粒内存在位错、孪晶缺陷;合金的共晶熔化激活能随形变率的增大而变小

当形变率达到40 %时

共晶熔化激活能下降很少;共晶熔化开始温度随形变率的增大略有下降。

Abstract

The effect of deformation rate on deformed microstructure of AZ91D magnesium alloy by the SIMA method was researched and differential scanning calorimetry （DSC） was employed to investigate the relation of deformation rate and eutectic melting activity energy.The results show that with the increase of deformation rate

the initial microstructure of the alloy changes from dendrites to fragmentary grains

in which there are twin crystals and dislocations

meanwhile the eutectic melting activity energy of the alloy decreases gradually.When the deformation rate is 40%

the eutectic melting activity energy is slightly decreases.The melting point of eutectic decreases slightly with the increase of deformation rate.

关键词

镁合金应变诱发熔化激活法（SIMA）形变率共晶熔化激活能形变组织DSC

Keywords

Mg AlloySIMADeformation RateEutectic Activity EnergyDeformed MicrostructureDSC

references

Alert me when the article has been cited

提交

Effects of Grain Distribution on Mechanical Properties of AZ80 Magnesium Alloy at Room Temperature

Micromorphology Control of TiO₂ Coating Prepared on Mg Alloy Stent

Pore Free Die Casting

Casting Magnesium Alloy of Mg Nd Zn Zr Series with Heat Resistance and High Strength

Research on a New Mg Alloy GQMZ96