ZA27 Alloy Castings with High Height-diameters Ratio in Squeezing Casting

Li Chenxi Cao Liang San Jingchao Xu Na Bai Yanhua Li Rongde

Views : 0 下载量: 89 CSCD: 7

Export
Share
Collection
Album

ZA27 Alloy Castings with High Height-diameters Ratio in Squeezing Casting
Issue 10, (2005)
Published： 2005 ，
DOI：

扫描看全文

[1]李晨希,曹亮,伞晶超,徐娜,白彦华,李荣德.挤压铸造ZA27合金大高径比铸件[J].特种铸造及有色合金,2005(10):41-43+6.

Li Chenxi Cao Liang San Jingchao Xu Na Bai Yanhua Li Rongde. ZA27 Alloy Castings with High Height-diameters Ratio in Squeezing Casting. [J]. Special Casting & Nonferrous Alloys (10).(2005)
[1]李晨希,曹亮,伞晶超,徐娜,白彦华,李荣德.挤压铸造ZA27合金大高径比铸件[J].特种铸造及有色合金,2005(10):41-43+6. DOI：

Li Chenxi Cao Liang San Jingchao Xu Na Bai Yanhua Li Rongde. ZA27 Alloy Castings with High Height-diameters Ratio in Squeezing Casting. [J]. Special Casting & Nonferrous Alloys (10).(2005) DOI：

摘要

通常挤压铸造仅适用于高径比小于3.5的铸件

研究大高径比铸件的挤压铸造将扩大这种先进铸造技术的应用范围。用试验和计算机模拟的方法

研究了高径比为7的ZA27合金铸件的力学性能、凝固过程中铸件内的温度、压力以及缩松的分布。结果表明

增加挤压铸造的压力不能有效地减少大高径比铸件的缩松缺陷;合理控制浇注温度和铸型预热温度能有效地消除大高径比铸件内的缩松

获得力学性能高且均匀的铸件。

Abstract

Generally

the squeezing casting is only employed for the castings whose height-diameter ratio is less than 3.5.Researching the castings with high height-diameter ratio in squeezing casting can extend the applicable scopes of the advanced casting technology.The mechanical properties of the ZA27 alloy with the high height-diameter ratio of 7 and distribution of temperature

pressure and shrinkage porosity during solidification process were investigated by experiment and numerical simulation.It is revealed that the shrinkage porosity in the castings with high height-diameter ratio can be obviously reduced with the increase of the pressure.Through rationally controlling pouring temperature

preheated temperature for mould and temperature distribution of the cast mould

the shrinkage porosity in the castings can be eliminated to obtain the castings with high and even mechanical properties.