Rolling Process of SiC Particulates Reinforced Heat Resistant Al-8.5 Fe-1.3 V-1.7 Si Aluminum Alloy
Issue 12, Pages: 765-767(2006)
Published： 2006 ，
DOI：

扫描看全文

[1]陈刚,尹显觉,贺毅强,陈志钢,陈振华.SiC颗粒增强Al-8·5Fe-1·3V-1·7Si的轧制工艺[J].特种铸造及有色合金,2006(12):765-767+748.

Chen Gang, Yin Xianiue, He Yiqiang, et al. Rolling Process of SiC Particulates Reinforced Heat Resistant Al-8.5 Fe-1.3 V-1.7 Si Aluminum Alloy. [J]. Special Casting & Nonferrous Alloys (12):765-767(2006)
[1]陈刚,尹显觉,贺毅强,陈志钢,陈振华.SiC颗粒增强Al-8·5Fe-1·3V-1·7Si的轧制工艺[J].特种铸造及有色合金,2006(12):765-767+748. DOI：

Chen Gang, Yin Xianiue, He Yiqiang, et al. Rolling Process of SiC Particulates Reinforced Heat Resistant Al-8.5 Fe-1.3 V-1.7 Si Aluminum Alloy. [J]. Special Casting & Nonferrous Alloys (12):765-767(2006) DOI：

摘要

研究了喷射沉积SiC颗粒增强Al-8·5Fe-1·3V-1·7Si板材的轧制工艺。探索了板材轧制过程中材料的密度变化规律及室温力学性能

通过金相、扫描电镜和透射电镜观察了其微观组织。研究表明

材料的致密化程度、轧制温度、轧制过程中道次压下量对材料的轧制性能有着重要影响。通过优化轧制工艺最终获得了良好的室温力学性能:490℃热轧材料的抗拉强度为535MPa

断后伸长率为7%。

Abstract

Rolling process of spray deposited SiC particulates reinforced Al-8. 5 Fe-1. 3 V-1. 7 Si aluminum sheet has been investigated. The density change and mechanical properties during the rolling process at ambient temperature were examined

and its microstructure was observed by SEM and TEM. It is found that the compactness

rolling temperature and pass reduction play a significant role in rolling properties of the composites. The composites with tensile strength of 35 MPa and elongation of 7% can be obtained by optimizing rolling processing parameters.