New Super-high Strength Aluminum Alloy in Low-frequency Electromagnetic Horizontal Continuous Casting
Issue 9, Pages: 706-708(2007)
Published： 2007 ，
DOI：

扫描看全文

[1]左玉波,崔建忠,赵志浩,李念奎,王洋,朱庆丰.低频电磁水平连铸新型超高强铝合金[J].特种铸造及有色合金,2007(09):706-708+654.

Zuo Yubo, Cui Jianzhong, Zhao Zhihao, et al. New Super-high Strength Aluminum Alloy in Low-frequency Electromagnetic Horizontal Continuous Casting. [J]. Special Casting & Nonferrous Alloys (9):706-708(2007)
[1]左玉波,崔建忠,赵志浩,李念奎,王洋,朱庆丰.低频电磁水平连铸新型超高强铝合金[J].特种铸造及有色合金,2007(09):706-708+654. DOI：

Zuo Yubo, Cui Jianzhong, Zhao Zhihao, et al. New Super-high Strength Aluminum Alloy in Low-frequency Electromagnetic Horizontal Continuous Casting. [J]. Special Casting & Nonferrous Alloys (9):706-708(2007) DOI：

摘要

在水平连铸过程中施加低频交变磁场

制备新型超高强铝合金铸锭

利用金相分析方法研究电磁场对铸锭质量的影响。结果表明

电磁场能提高铸锭表面质量

减少宏观偏析

细化宏观和微观组织。低频电磁水平连铸新型超高强铝合金铸锭经过挤压和热处理后屈服强度为742MPa

抗拉强度为758MPa

伸长率为8.5%。

Abstract

New super-high strength Al alloy ingot was fabricated by horizontal continuous casting with low frequency alternative electromagnetic field. Effects of electromagnetic field on quality of aluminum alloy ingot were observed by the metallography method. The results reveal that electromagnetic field can improve the quality of the ingot through reducing macro-segregation and refining micro-macro structure. The yield strength

tensile strength and elongation of the LFEHC new super-high aluminum alloy reach 742 MPa

758 MPa and 8.5%

respectively

after heat treatment based on squeezing casting.