Effects of Injection Temperature on Microstructure and Mechanical Properties of ADC12 Aluminum Alloy in Super Slow Speed Die Casting

Ji Lianqing1; Ji Peiying1; Xiong Shoumei2; Masayuki Murakami3; Yoshihide Matsumoto3; Shingo Ikeda3

Views : 0 下载量: 382 CSCD: 5

Export
Share
Collection
Album

Effects of Injection Temperature on Microstructure and Mechanical Properties of ADC12 Aluminum Alloy in Super Slow Speed Die Casting
Issue 7, Pages: 529-531(2008)
Published： 2008 ，
DOI：

扫描看全文

[1]纪莲清,纪培英,熊守美,村上正幸,松本悦豪,池田伸吾.浇注温度对ADC12合金超低速压铸件组织性能的影响[J].特种铸造及有色合金,2008(07):529-531+489.

Ji Lianqing1, Ji Peiying1, Xiong Shoumei2, et al. Effects of Injection Temperature on Microstructure and Mechanical Properties of ADC12 Aluminum Alloy in Super Slow Speed Die Casting. [J]. Special Casting & Nonferrous Alloys (7):529-531(2008)
[1]纪莲清,纪培英,熊守美,村上正幸,松本悦豪,池田伸吾.浇注温度对ADC12合金超低速压铸件组织性能的影响[J].特种铸造及有色合金,2008(07):529-531+489. DOI：

Ji Lianqing1, Ji Peiying1, Xiong Shoumei2, et al. Effects of Injection Temperature on Microstructure and Mechanical Properties of ADC12 Aluminum Alloy in Super Slow Speed Die Casting. [J]. Special Casting & Nonferrous Alloys (7):529-531(2008) DOI：

摘要

应用简单圆形拉伸试样

研究了浇注温度对ADC12铝合金超低速压铸件性能的影响

以优化超低速压铸工艺及其参数。试验结果表明

在超低速试验条件下

各种浇注温度下铸件的密度都比普通压铸要高;浇注温度有最佳值

最佳值的大小和模具温度、脱模剂有关。在超低速基准试验条件下

浇注温度的最佳值为700℃

此时合金中的初生α-Al为树枝晶状

与较高浇注温度时相比

一次和二次枝晶臂明显变小或变短

铸件性能较高。

Abstract

In order to optimize the super slow speed （SSS） die casting process

effects of pouring temperature on mechanical properties of ADC12 magnesium alloy in SSS die casting were examined with a standard tensile testing specimen. The results show that the density of specimen in SSS die casting is higher than that in conventional die castings at various pouring temperatures. There exists a critical value for pouring temperature

which is closely related to die temperature and releasing agent. The desirable pouring temperature is 700 ℃ under the SSS condition

and the dendrite primary α-Al phase can be observed in the alloy at the pouring temperature. Compared with that in the alloy poured at higher temperature

the primary and secondary dendritic arm becomes shorter in the alloy

exhibiting better tensile properties.