Microstructure Feature and Dynamic Softening Behavior of Aluminnum Sheet Used for Easy-open Can During Hot Deformation

Wang Huosheng1; Fu Gaosheng2; Chen Yonglu1; Chen Hong-ling3

Views : 0 下载量: 89 CSCD: 1

Export
Share
Collection
Album

Microstructure Feature and Dynamic Softening Behavior of Aluminnum Sheet Used for Easy-open Can During Hot Deformation
Issue S1, Pages: 208-210(2008)
Published： 2008 ，
DOI：

扫描看全文

[1]王火生,傅高升,陈永禄,陈鸿玲.易拉罐用铝材热变形过程中的微观组织特征与动态软化[J].特种铸造及有色合金,2008(S1):208-210.

Wang Huosheng1, Fu Gaosheng2, Chen Yonglu1, et al. Microstructure Feature and Dynamic Softening Behavior of Aluminnum Sheet Used for Easy-open Can During Hot Deformation. [J]. Special Casting & Nonferrous Alloys (S1):208-210(2008)
[1]王火生,傅高升,陈永禄,陈鸿玲.易拉罐用铝材热变形过程中的微观组织特征与动态软化[J].特种铸造及有色合金,2008(S1):208-210. DOI：

Wang Huosheng1, Fu Gaosheng2, Chen Yonglu1, et al. Microstructure Feature and Dynamic Softening Behavior of Aluminnum Sheet Used for Easy-open Can During Hot Deformation. [J]. Special Casting & Nonferrous Alloys (S1):208-210(2008) DOI：

摘要

采用热模拟试验技术和TEM分析

探讨了易拉罐用铝材在不同变形条件下的微观组织特征和动态软化行为。结果表明

应变速率为0.1s-1时

若变形温度较低

则发生了动态回复。若变形温度高于723K

产生明显的动态再结晶;变形温度为673K时

在低应变速率条件下

产生动态再结晶

变应速率高于0.1s-1

软化过程具有动态回复和动态再结晶的混合特征

当应变速率高于5.0s-1时

产生几何动态再结晶。

Abstract

The characters of microstructure and dynamic softening behavior of aluminum sheet used for easy-open can during hot deformation were studied and the dynamic softening behavior were discussed. The results show that dynamic recovery occurs at low temperature with a stain rate of 0.1 s-1 and dynamic recrystallization takes place when the temperature is higher than 723 K。Dynamic recrystallization occurs at low strain rate when the temperature is 673 K. With the increase of strain rate

dynamic recovery and dynamic recrystallization take place at the same time. However

geometry dynamic recrystallization occurs when strain rate is higher than 5.0s-1.