Effects of Er and Nd on Microstructure and Properties of Mg-0.6Zr Alloy

Liu Xianlan1; Liu Chuming1; Li Huizhong1; Zhang Wenyu2; Zeng Sumin1

Views : 0 下载量: 148 CSCD: 4

Export
Share
Collection
Album

Effects of Er and Nd on Microstructure and Properties of Mg-0.6Zr Alloy
Vol. 29, Issue 2, Pages: 173-175(2009)
Published： 2009 ，
DOI：

扫描看全文

[1]刘先兰,刘楚明,李慧中,张文玉,曾苏民.Er、Nd对Mg-0.6Zr合金组织和性能的影响[J].特种铸造及有色合金,2009,29(02):173-175+96-97.

Liu Xianlan1, Liu Chuming1, Li Huizhong1, et al. Effects of Er and Nd on Microstructure and Properties of Mg-0.6Zr Alloy. [J]. Special Casting & Nonferrous Alloys 29(2):173-175(2009)
[1]刘先兰,刘楚明,李慧中,张文玉,曾苏民.Er、Nd对Mg-0.6Zr合金组织和性能的影响[J].特种铸造及有色合金,2009,29(02):173-175+96-97. DOI：

Liu Xianlan1, Liu Chuming1, Li Huizhong1, et al. Effects of Er and Nd on Microstructure and Properties of Mg-0.6Zr Alloy. [J]. Special Casting & Nonferrous Alloys 29(2):173-175(2009) DOI：

摘要

采用金相显微镜、扫描电镜及能谱分析等手段

研究了Er、Nd对铸态Mg-0.6Zr合金的组织和常温力学性能的影响。结果表明

Er、Nd对Mg-Zr镁合金组织均有细晶强化和固溶强化作用

提高了合金的力学性能。Mg-0.6Zr合金中添加Nd、Er后晶粒尺寸由300μm分别细化至80μm和50μm左右。添加0.94%的Nd后

Mg-0.6Zr合金的抗拉强度和伸长率分别提高了13.87%和137.1%

屈服强度基本不变。而添加1.09%的Er后

Mg-0.6Zr合金的抗拉强度、屈服强度和伸长率分别提高了11.16%、11.94%和2.35%。复合加入Er和Nd时

合金的抗拉强度同单独加入Er后合金的抗拉强度相当

屈服强度和伸长率略有下降。

Abstract

Microstructure and mechanical properties of Mg-0.6Zr alloys containing Er and Nd were investigated by optical microscope（OM）

scanning electron microscope（SEM）and energy spectrum analysis.The results reveal that mechanical properties of the Mg-0.6Zr alloy can be distinctly improved with Er and Nd addition as a result of grain refinement strengthening and solution strengthening.Grain size in microstructure of the alloy can be refined from 300 μm to 80 μm and 50 μm with Er or Nd addition.Tensile strength and elongation of the Mg-0.6Zr alloy with 0.94% Nd addition can be increased by 13.87% and 137.6%

respectively

with the slight change of yield strength

compared with those of matrix alloy

while those of the alloy with 1.09% Er addition can be increased by 11.16%

11.94% and 2.35%

respectively.Tensile strength of the alloy with mixed Er and Nd addition is equivalent to that of the alloy with Er addition

however

yield strength and elongation are somewhat declined.