Effects of Aluminum Content on the Microstructure and Mechanical Properties of AZ Magnesium Alloys
Vol. 29, Issue 9, Pages: 848-850(2009)
Published： 2009 ，
DOI：

扫描看全文

[1]张广俊,龙思远,曹凤红.Al含量对AZ系镁合金组织和力学性能的影响[J].特种铸造及有色合金,2009,29(09):848-850+782.

Zhang Guangjun1, Long Siyuan2, Cao Fenghong1. Effects of Aluminum Content on the Microstructure and Mechanical Properties of AZ Magnesium Alloys. [J]. Special Casting & Nonferrous Alloys 29(9):848-850(2009)
[1]张广俊,龙思远,曹凤红.Al含量对AZ系镁合金组织和力学性能的影响[J].特种铸造及有色合金,2009,29(09):848-850+782. DOI：

Zhang Guangjun1, Long Siyuan2, Cao Fenghong1. Effects of Aluminum Content on the Microstructure and Mechanical Properties of AZ Magnesium Alloys. [J]. Special Casting & Nonferrous Alloys 29(9):848-850(2009) DOI：

摘要

以AZ61、AZ71、AZ81镁合金作为研究对象

研究了Al含量对镁合金的组织结构与力学性能的影响。结果表明

随着Al含量的增加

镁合金微观组织中分布在α-Mg固溶体间的β-Mg17Al12金属间化合物数量增加

分布更加连续

当Al含量达到8%时

α-Mg初生相的连续性被割裂;合金力学性能变化与组织结构特征紧密相关

AZ71镁合金具有较好的室温力学性能

铸态时抗拉强度为211.63MPa

屈服强度为109.84MPa

伸长率为7.20%

固溶处理后抗拉强度达到235.98MPa

屈服强度达到122.12MPa

伸长率为14.72%;试样中脆性β-Mg17Al12金属间化合物的分布对于裂纹的扩展具有重要影响

铸态AZ系镁合金室温拉伸断口均表现为脆性断裂。

Abstract

Effects of different Al contents on microstructure and mechanical properties of AZ series magnesium alloys were investigated. The results reveal that with increasing in Al content

numbers of Mg17Al12 phase distributed into α-Mg phase are increased with more continuous distribution in microstructure of Mg alloy

however

with 8% Al content

the α-Mg phase is isolated by the network Mg17Al12 phase. The mechanical properties of the alloy are closely related to the microstructure characteristics of α-Mg phase and Mg17Al12 phase. AZ71 magnesium alloy exhibits the best mechanical properties among three types of alloys. As-cast tensile strength

yield strength and elongation of the AZ71 alloy reach 211.63MPa

109.84MPa and 7.20%

respectively

and after solid solution treatment

tensile strength

yield strength and elongation reach 235.98MPa

122.12MPa and 14.72%

respectively. The distribution of brittle Mg17Al12 phase greatly affects crack propagation in tensile samples. The fracture morphologies of all AZ series alloys are characterized by brittle fracture.