Origination of Slag Inclusion in EPC Steel Casting

Li Zengmin1; Li Lixin1; Zhang Tiantian2

切换中文

Views : 26 Downloads: 295 CSCD: 2

Export
Share with wechat friends or circle of friends

Share
Collection
Album

Origination of Slag Inclusion in EPC Steel Casting
- role： First author 第一作者
- Affiliation：
  School of Materials Science and Engineering, Hebei University of Science and Technology,Shijiazhuang,China
Li Zengmin1
1 ,
- Affiliation：
  School of Materials Science and Engineering, Hebei University of Science and Technology,Shijiazhuang,China
Li Lixin1
1 ,
- Affiliation：
  Shijiazhuang Estate Development and Construction General Company,Shijiazhuang,China
Zhang Tiantian2
2
Vol. 31, Issue 3, Pages: 245-247(2011)
Published： 2011 ，
DOI：

Scan for full text

Quote
[1]李增民,李立新,张田田.消失模铸钢件夹渣缺陷的形成机理分析[J].特种铸造及有色合金,2011,31(03):245-247+192.

Li Zengmin1, Li Lixin1, Zhang Tiantian2. Origination of Slag Inclusion in EPC Steel Casting. [J]. Special Casting & Nonferrous Alloys 31(3):245-247(2011)
[1]李增民,李立新,张田田.消失模铸钢件夹渣缺陷的形成机理分析[J].特种铸造及有色合金,2011,31(03):245-247+192. DOI：

Li Zengmin1, Li Lixin1, Zhang Tiantian2. Origination of Slag Inclusion in EPC Steel Casting. [J]. Special Casting & Nonferrous Alloys 31(3):245-247(2011) DOI：

Abstract

The slag inclusion and gas hole defects were generated easily in EPC steel castings. The source, shape distribution and position where slag inclusion easily occur were analyzed. According to the filling behavior of molten steel, influence of the turbulent flow and wall attachment effects of filling molten steel on formation of slag inclusion were approached. Based on the thermodynamics and kinetics, the forming and floating mechanism of the slag inclusion in EPC steel castings were described. The approaches and ways of eliminating slag inclusion in EPC steel castings were presented.

transl

Keywords

EPC Steel Casting; Slag Inclusion; Forming and Discharging Mechanism

transl

摘要

消失模铸钢件极易产生夹渣及气孔缺陷。分析了消失模铸钢件夹渣缺陷的来源、形态分布、易出现的部位。从钢水充型形态分析出发

分析了充型钢水的湍流状态及附壁效应对夹渣形成的影响。从热力学和动力学角度分析了消失模铸钢件夹渣缺陷形成及移动机理

提出了消失模铸钢件减少夹渣缺陷的途径和建议。

Abstract

The slag inclusion and gas hole defects were generated easily in EPC steel castings. The source

shape distribution and position where slag inclusion easily occur were analyzed. According to the filling behavior of molten steel

influence of the turbulent flow and wall attachment effects of filling molten steel on formation of slag inclusion were approached. Based on the thermodynamics and kinetics

the forming and floating mechanism of the slag inclusion in EPC steel castings were described. The approaches and ways of eliminating slag inclusion in EPC steel castings were presented.

关键词

消失模铸钢件夹渣缺陷形成及排出机理

Keywords

EPC Steel CastingSlag InclusionForming and Discharging Mechanism

references

Alert me when the article has been cited

Submit

No data

Related Author

No data

Related Institution

No data

⁰