Effects of Na2WO4 and SiCp on Micro-arc Oxidation Coatings on 2A12 Aluminum Alloy

Li Yuhai1; Zhao Yan1; Zhao Hui1; Xing Guihe1

Views : 0 下载量: 260 CSCD: 3

Export
Share
Collection
Album

Effects of Na₂WO₄ and SiC_p on Micro-arc Oxidation Coatings on 2A12 Aluminum Alloy
Vol. 31, Issue 2, Pages: 187-190(2011)
Published： 2011 ，
DOI：

扫描看全文

[1]李玉海,赵艳,赵晖,邢贵和.Na_2WO_4和SiC_p对2A12铝合金微弧氧化膜的影响[J].特种铸造及有色合金,2011,31(02):187-190+206.

Li Yuhai1, Zhao Yan1, Zhao Hui1, et al. Effects of Na₂WO₄ and SiC_p on Micro-arc Oxidation Coatings on 2A12 Aluminum Alloy. [J]. Special Casting & Nonferrous Alloys 31(2):187-190(2011)
[1]李玉海,赵艳,赵晖,邢贵和.Na_2WO_4和SiC_p对2A12铝合金微弧氧化膜的影响[J].特种铸造及有色合金,2011,31(02):187-190+206. DOI：

Li Yuhai1, Zhao Yan1, Zhao Hui1, et al. Effects of Na₂WO₄ and SiC_p on Micro-arc Oxidation Coatings on 2A12 Aluminum Alloy. [J]. Special Casting & Nonferrous Alloys 31(2):187-190(2011) DOI：

摘要

在质量浓度为40g/L的Na2SiO3

8g/L的Na2WO4混合电解液中添加SiCp

在2A12铝合金基体上原位生长微弧氧化陶瓷膜。采用扫描电子显微镜（SEM）、能谱分析仪（EDS）、X射线衍射仪（XRD）分析了陶瓷膜微观形貌、元素含量、相组成

通过数字式覆层测厚仪和摩擦磨损试验检测了氧化膜的厚度和耐磨性。结果表明

Na2SiO3、Na2WO4混合电解液生长的陶瓷膜由α-Al2O3和mullite相组成

膜层较致密

Na2WO4的加入提高了膜层生长速率;添加SiC微粒后

微弧氧化过程中SiC微粒分解

促进莫来石相形成

膜层有较好的耐磨性。

Abstract

Ceramic oxide coatings were prepared on 2A12 aluminum alloy by micro arc oxidation in 40 g/L Na2SO3 and 8 g/L Na2WO4 mixed electrolyte with SiC particle addition.Micro-morphology

phase constituent and chemical composition of the coating were analyzed by SEM（scanning electron microscope）

EDS（energy dispersive spectrometer）

XRD（X-ray diffraction）.Thickness and wear resistance of the coating were measured by the digital thickness meter and friction wear testing.The results show that the coating consists of α-Al2O3 and mullite phase in Na2SiO3 and Na2WO4 electrolyte

and Na2WO4 can promote compact growth of the coating.SiC particle is decomposed in the process of microarc oxidation

promoting the formation of mullite phase.The coatings ware preferable abrasive resistance.

关键词

微弧氧化Na2WO4SiCp铝合金摩擦磨损

Keywords

Micro-arc OxidationNa2WO4SiC ParticleAluminum AlloyFriction and Wear

references

Alert me when the article has been cited

提交

Biotribological Behaviors of Micro-arc Oxidation Film on Zircalloy-4

Effects of In-situ TiB₂ Particles on Microstructure and Mechanical Properties of AlSi10Mg Alloy

Effects of Cr-Fe Particle Size on Friction and Wear Properties of Copper-based Powder Metallurgy Materials

Integrated Aluminum Alloy Die Casting Process for Automobile Body

Application of ACSR in Aluminum Alloys with High Thermal Conductivity and Strength