Analysis and Control of Crack Defects in Centrifugal Casting Compound Roll Barrel

Gao Yuzhang

Views : 0 下载量: 130 CSCD: 1

Export
Share
Collection
Album

Analysis and Control of Crack Defects in Centrifugal Casting Compound Roll Barrel
Vol. 31, Issue 7, Pages: 646-647(2011)
Published： 2011 ，
DOI：

扫描看全文

[1]高玉章.离心复合轧辊辊身裂纹缺陷分析与控制[J].特种铸造及有色合金,2011,31(07):646-647.

Gao Yuzhang. Analysis and Control of Crack Defects in Centrifugal Casting Compound Roll Barrel. [J]. Special Casting & Nonferrous Alloys 31(7):646-647(2011)
[1]高玉章.离心复合轧辊辊身裂纹缺陷分析与控制[J].特种铸造及有色合金,2011,31(07):646-647. DOI：

Gao Yuzhang. Analysis and Control of Crack Defects in Centrifugal Casting Compound Roll Barrel. [J]. Special Casting & Nonferrous Alloys 31(7):646-647(2011) DOI：

摘要

采用离心铸造生产高镍铬钼复合轧辊

其辊身常出现裂纹缺陷

成为制约产品质量提高的重要影响因素。通过对辊身裂纹的特征及产生原因的分析

提出了应对措施

有效地控制和减少了辊身裂纹缺陷

提高了产品合格率。

Abstract

High nickel chrome molybdenum compound ductile iron roller was produced by centrifugal casting. Crack defects often appeared in the roll barrel

which became the important influencing factors to restrain the improvement of product quality. Through analyzing the characteristics and origination of crack in the roll barrel

the countermeasures were put forward. Through the countermeasures

crack in the roll barrel is effectively controled and decreased

increasing the qualification rate of the roller.