Influence of Carbon Content on the Microstructure of In-Situ TiC Particualte Reinforced Fe Matrix Composite
Issue 2, Pages: 8-9(2001)
Published：2001
DOI：
稿件说明：

移动端阅览

[1]章桥新,梅志,杨勇勤.碳含量对TiC颗粒增强铁基复合材料微观结构的影响[J].特种铸造及有色合金,2001(02):8-9+6. DOI：

Zhang Qiaoxin. Influence of Carbon Content on the Microstructure of In-Situ TiC Particualte Reinforced Fe Matrix Composite[J]. Special Casting & Nonferrous Alloys, 2001, (2): 8-9. DOI：

摘要

采用分析电镜和X射线衍射仪研究了原位合成TiC颗粒增强铁基复合材料的微观结构

结果表明所形成的颗粒增强相为非化学式的TiCxN1-x

其中x值大小随基体含碳量的高低而发生明显变化

基体中较高的含碳量有助于抑制Fe2 Ti相的形成

Abstract

The microstructure of in situ TiC particulate reinforced Fe matrix composite was analyzed by means of TEM and XRD. The results showed that particulate reinforced phase was non stoichiometric TiC x N 1- x

in which the x value greatly depended on the variation of carbon content in matrix. The higher carbon content in matrix is helpful to restrain the formation of Fe 2Ti phase.

关键词

Keywords

references

Alert me when the article has been cited

提交

Effects of Scanning Speed on Microstructure and Properties of SLMed Ti-6Al-4V Alloy

Isothermal Crystallization Kinetics of Zr₅₀Cu₃₄Al₈Ag₈ Amorphous Alloy

Effects of Remelting without Fusion Agent on Microstructure and Properties of Prefabricated Ingots of ZM6 Magnesium Alloy

Microstructure and Properties of SiC/Al-Mg Composites Based on 3D-printed Preforms