    • Effects of Aging Temperature on Microstructure and Properties of Al-9Si-2Cu-xFe Alloys

    • “In the field of Al-9Si-2Cu alloys, the microstructure and properties of alloys with different Fe contents were studied at different aging temperatures. It was found that the alloy strength was highest after aging treatment at 175 ℃ for 2 hours, reaching 304 MPa.”
    • Vol. 45, Issue 2, Pages: 273-278(2025)   

      Received：01 January 2024，

      Revised：08 February 2014，

      Accepted：2024-02-04，

      Published：20 February 2025

    • DOI： 10.15980/j.tzzz.T20240001     

    移动端阅览

  • LI Y S，CHEN J S，TANG C Y，et al. Effects of aging temperature on microstructure and properties of Al-9Si-2Cu-xFe alloys［J］. Special Casting & Nonferrous Alloys，2025，45（2）：273-279. DOI： 10.15980/j.tzzz.T20240001.
  •  
  •  
Alert me when the article has been cited
提交

相关文章

相关作者

ZHAO Dan 中国机械总院集团宁波智能机床研究院有限公司
JIA Fei 中国机械总院集团宁波智能机床研究院有限公司
ZHANG Lei 中国机械总院集团宁波智能机床研究院有限公司;新型钎焊材料与技术国家重点实验室，郑州机械研究所有限公司;清华大学机械工程系
CHENG Zhan 中国机械总院集团宁波智能机床研究院有限公司
FAN Zhibin 中国机械总院集团宁波智能机床研究院有限公司
JIU Yongtao 宁波中机松兰刀具科技有限公司
LIU Wenjing 兰州理工大学省部共建有色金属先进加工与再利用国家重点实验室
LI Yuandong 兰州理工大学省部共建有色金属先进加工与再利用国家重点实验室;兰州理工大学有色金属合金及加工教育部重点实验室

相关机构

China Academy of Machinery Ningbo Academy of Intelligent Machine Tool Co.， Ltd.
State Key Laboratory of New Brazing Materials and Technology， Zhengzhou Machinery Research Institute Co.， Ltd.
Department of Mechanical Engineering， Tsinghua University
Ningbo Zhongji Songlan Cutting Tool Technology Co.， Ltd.
State Key Laboratory of Advanced Processing and Recycling of Nonferrous Metals， Lanzhou University of Technology
0